ABSTRACT
At present, the filtration of virus and other small particles in the air by meltblown cloth produced by electret treatment mainly depends on its electrostatic adsorption mechanism. However, because the surface charge of melt blown fabric can not be maintained for a long time, it can not maintain high efficiency filtration for a long time. Therefore, there is no guarantee for the medical staffs to not be infected by COVID-19. Therefore, it is necessary to improve the mechanical filtration efficiency of melt blown fabric in the situation of an electric charge loss. In this paper, nylon 6 (PA6) nanofibers were electrospun on melt blown cloth by electrospinning technology, and a sandwich material with melt blown cloth as surface layer and PA6 nanofibers as middle layer was made by hot- pressing technology;the surface morphology, thermal and mechanical properties of the sandwich material were characterized, and its filtration performance was tested. The experimental results show that the surface integrity of the sandwich material is high, and the diameter of nanofibers can reach about 67 nm;without the electret treatment, the filtration efficiency of the sandwich material for particles in an size of 0.2 μm is more than 95%,while the filtration efficiency of non-woven fabric is zero;the filtration resistance of the material is about 284 Pa, which is suitable for personal protection. © 2023 Chengdu University of Science and Technology. All rights reserved.
ABSTRACT
The transmission of pathogens via surfaces poses a major health problem, particularly in hospital environments. Antimicrobial surfaces can interrupt the path of spread, while photocatalytically active titanium dioxide (TiO2) nanoparticles have emerged as an additive for creating antimicrobial materials. Irradiation of such particles with ultraviolet (UV) light leads to the formation of reactive oxygen species that can inactivate bacteria. The aim of this research was to incorporate TiO2 nanoparticles into a cellulose-reinforced melamine-formaldehyde resin (MF) to obtain a photocatalytic antimicrobial thermoset, to be used, for example, for device enclosures or tableware. To this end, composites of MF with 5, 10, 15, and 20 wt% TiO2 were produced by ultrasonication and hot pressing. The incorporation of TiO2 resulted in a small decrease in tensile strength and little to no decrease in Shore D hardness, but a statistically significant decrease in the water contact angle. After 48 h of UV irradiation, a statistically significant decrease in tensile strength for samples with 0 and 10 wt% TiO2 was measured but with no statistically significant differences in Shore D hardness, although a statistically significant increase in surface hydrophilicity was measured. Accelerated methylene blue (MB) degradation was measured during a further 2.5 h of UV irradiation and MB concentrations of 12% or less could be achieved. Samples containing 0, 10, and 20 wt% TiO2 were investigated for long-term UV stability and antimicrobial activity. Fourier-transform infrared spectroscopy revealed no changes in the chemical structure of the polymer, due to the incorporation of TiO2, but changes were detected after 500 h of irradiation, indicating material degradation. Specimens pre-irradiated with UV for 48 h showed a total reduction in Escherichia coli when exposed to UV irradiation.